Carbon cast steels

Własności mechaniczne (minimalne) / Mechanical properties (minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
L-20 PN-89/H-83157 N 245 440 – 590 22 49 125 – 165
L-400 PN-85/H-83152 N 250 400 25 40 60 114 – 156
L450 PN-85/H-83152 N 260 450 22 30 50 126 – 170
L500 PN-85/H-83152 N 320 500 18 25 45 140 – 197
L600 PN-85/H-83152 N 360 600 16 21 40 160 – 212
L650 PN-85/H-83152 N 380 650 15 18 35 170 – 230
GS-C25 DIN 17245 N 245 440-590 22 27 150
U 40
GS-38 DIN 1681 N 200 380 25 40 35
GS-45 DIN 1681 N 230 450 22 31 27
GS-52 DIN 1681 N 260 520 18 25 22
GS-60 DIN 1681 N 300 600 15 21 20
GS-70 DIN 1681 N 420 700 12
GS-CK45 1.1191 U 370 630 – 780 17 45 25 175 – 210
GP240GH EN 10213-2 N 240 420-600 22 27
U 240 420-600 22 40 27 (-50 °C)
200-400W N 200 25 40 45
PN-ISO 3755 400 – 550
200-400 30
230-450W N 230 22 31 45
PN-ISO 3755 450 – 600
230-450 25
270-480W N 270 18 25 22
PN-ISO 3755 480 – 630
270-480 22
340-550W N 340 15 21 20
PN-ISO 3755 550 – 700
340-550 20
WCB ASTM A 216 N N U 250 485 – 655 485 – 600 22 35 35 20 (-18°C) 27 (-29° C)
LCB ASTM A 352 U 240 450 – 620 24 35 18
14 (-46 oC)
LCC ASTM A 352 U 275 485 – 655 A4 = 22 35 20
16 (-46 oC)
GS240 EN 10293 N 240 450 22 31
2005 600
GE240 EN 10293 N 240 450 22 27
2005 600
G28Mn6 S.A. 3071 120 N 260 520 18 27 149 –
K2 670 201
GE300 S.A. 3071 120 N 300 570 15 31 163-
K8 720 217

Abrasion resistant low-alloy cast steels

Własności mechaniczne (minimalne) / Mechanical properties (minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISOV HB
MPa MPa % % J/cm2 J
GS-16Mn5 DIN 17182 N 230 430 – 600 25 45
L20G PN-97/H-83156 N 300 550 18 25 49 160
U 340 550 14 25 39 180
GS-20Mn5 DIN 17182 N 260 500 22 40
U 300 650 24 50
G20Mn5 EN 10213 N 300 500 22 20 50
650 27 (-30°C)
U 24 22 27 (-40°C)
Gs21Mn5 SEW 685 U 300 480 -620 20 35 (-30°)
GS-24Mn6 SEW 520 U 400 600 – 750 18 60
27 (-30°)
A-4 BS 3100 N 320 540 16 30 152 – 207
L30GS PN-97/H-83156 N 350 600 14 25 29 175
U 390 650 14 30 49 200
A-6 BS 3100 UI 530 740 13 25 220-255
UII 495 690 – 850 201-255
6BM (BT2) BS 3100 U 585 850 8 25 248 – 327
GS-30Mn5 DIN 17205 N 260 520 – 670 18 32
U 360 500 – 650 12 35
L35GSM PN-88/H-83160 U 850 1100 8 18 300
L35HGS PN-97/ H-83156 NO 350 600 14 25 29 190
U 590 790 10 20 39 230
Gs45CrV6 wg.specyfikacji N 450 700 14
L40H3T PN-88/H-83160 N 600 1000 8 14 14 220
L180HNM PN-90/H-83161 N 240
L30HGSM PIOMA U 400
L20HGSNM PN-88/H-83160 N 290-340
U 388-477
SC-06 wg.specyfikacji U 690 965 8 25 302 – 340
L35HNM PN-97/H-83156 N 550 800 12 270
U 550 750 15 25 39
L35G PN-97/H-83156 N 300 550 12 20 29 180
U 350 600 14 30 49 200
L45G PN-88/H-83160 N 450 750 15 30 200
U 650 850 10 30 250
L40GM PN-88/H-83160 N 450 750 14 30 200
U 700 850 10 30 250
G17CrMo9-10 EN 10213 NO 400 590 -740 18 40
L70H2GNM PN-90/H-83161 N O 240-400

Llow-alloy cast steels for construction purposes

Własnosci mechaniczne (minimalne) / Mechanical properties (minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
L35GMA ZN-93/ HSW/0596 U 414 620 15 35 187 – 241
L20HGNM ZN-93/ HSW/0596 UI 414 620 15 35 187-241
II 586 724 16 35 217-269
III 655 827 13 30 255-302
L25HGNM ZN-93/ HSW/0596 UI 414 620 15 35 187-241
II 586 724 16 35 217-269
III 655 827 13 30 255-302
L35HGNMA ZN-93/ HSW/0596 UI 414 620 15 35 187-241
II 586 724 16 35 217-269
III 655 827 13 30 255-302
IV 862 1034 9 22 302-363
L25GN PIOMA N 380 570 18 45 70 156
U 550 700 18 45 70 190
L35GN PN-97/ H-83156 N 400 650 18 30 45
U 750 900 12 25 40 270
L25GNF PIOMA U 650 800 14 25 40 240
L20GNMF PIOMA U 700 850 10 25 40 220
L25GNMF PIOMA U 800 950 10 25 40 280
L35GNMF PIOMA U 900 1100 8 25 30 320
L17HMF PN-89/H-83157 NO 440 590 -780 15 39 165 – 242
GS-17CrMoV511 DIN 17245 NO 440 590 -780 15 27
L17HM PN-97/H-83156 N 275 485 18 35
U 245 590 18 39 175
L20HM PN-89/H-83157 NO 400 600 15 39 190
L25HM PN-97/ H-83156 N 260 450 20 22 31 170
U 310 600 16 25 34 195
L35HM PN-97/ H-83156 N 290 550 18 25 31 180
U 550 750 14 30 27 205
L40HM PN-88/H-83160 U 850 1000 8 20 400
S22Mo wg.specyfikacji U 300 490 – 620 19 45 30 145 – 190
GS-17CrMo5-5 DIN 17245 NO 315 490 -640 20 39 27 125 -165
G17CrMo5-5 EN 10213 NO 315 490 -690 20 39 27 125 -170
L18HM PN-89/H-83157 NO 440 590 – 780 15 39 125 -165
GS-12MnNiMo5,5 PIOMA U 475 600 17
GS-20CrMo5 PIOMA U 475 675
GS-22Mo4 DIN 17245 U 245 440 – 590 22 27
Gs25CrMo4 N 300 550-700 16 27
DIN 17245 U 450 600-750 14 40
550 700-850 10 32
GS-34CrMo4 N 380 650-800 10 16
DIN 17245 U 540 700-850 12 30
355 550 27
GS-42CrMo4 DIN 17205 N 400 700-850 10 12
UI 600 800-950 12 30
I 650 780-930 14 35
UII 700 850-1000 10 27
II 800 900-1000 10 27
Gs18NiMoCr36 SEW 520 U 630 780 – 930 12 40
L30H PN-97/H-83156 N 300 550 15 30 27 170
U 440 700 15 30 41 190
GS-18NiCrMo86V wg.specyfikacji
acc to specification
U 800 950 – 1100 10 20
GS-34CrNiMo6 SEW515 N 550 800 32
DIN 17205 950 12
G20Mo5 EN 10213 U Re0,2 440 22 27
245 590
115-95 specy. A148 U 665 795 15 30 248
286
120-110 specy. CMS-01 U 759 827 12 30 42 J (32) -20 °C 269
302
135-125 specy. CMS-01 U 861 930 12 25 33 J (26) 277
-20 °C 332
specy. WS-236 U 862 931 14 45 42 J (26)
1103 -40 °C 341
LC1 ASTM A 352 U 240 450 A4 35 18 J ( 14 )
620 24 -59 °C
30 J
-60 °C

Abrasion resistant high-alloy mangan cast steels

Własnosci mechaniczne ( minimalne) / Mechanical properties ( minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
L120G13 PN-88/H-83160 P 170 – 217
Gx120Mn13 P
A ASTM/A128 P
C ASTM/A128 P
G-X120MnCr182 PIOMA P
L120G13H PN-88/H-83160 P 170 – 241

Abrasion resistant high-alloy cast steels

Własnosci mechaniczne ( minimalne) / Mechanical properties ( minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
L100H 6 M PN-88/H 83160 U 495 – 601
L40 H 5 MF PN-90/H-83161 N min.200

Tool high-alloy cast steels

Własnosci mechaniczne ( minimalne) / Mechanical properties ( minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
L210H21S PN-90/H-83161 Z 380
L35H17N2M PN-90/H-83161 N 400-500
NO 290-350

Corrosion resistant high-alloy cast steels

Własnosci mechaniczne ( minimalne) / Mechanical properties ( minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
LH14 PN-86/H-83158 NO 390 580 12 30 170 – 230
780
LH18N9 PN-88/H-83158 P 180 440 30 40 80 130 – 190
640
GX6CrNi 18 9 DIN 17445 P 200 440 20 60
640
Gx5CrNi13-4 DIN 17445 U 550 760 15 50 240 – 300
960
CA6NM ASTM A487 U 550 760 A4 35 50
930 15
CF 8 M ASTM A351/351M P 210 440 460 20 60
GX 6 CrNiMo1810 DIN 17445 P 210 440 460 20 60

Heat resistant high-alloy cast steel

Własnosci mechaniczne ( minimalne) / Mechanical properties ( minimal)
Gatunek / Grade Norma / Standard Obróbka cieplna / Heat treatment Re Rm A5 Z KCU3 ISO-V HB
MPa MPa % % J/cm2 J
G-X40CrSi13 DIN 17465 Z 200 – 300
LH26 PN-90/H-83159 Z 300 400 250 – 350
G-X40CrSi29 DIN 17465 S 200 – 300
LH18S2 PN-90/H-83159 Z 420 250 – 350
LH23N18G PN-90/H-83159 N 250 550 25 155 – 250
LH25N19S2 PN-90/H-83159 N 250 550 25 155 – 200
LH26N4S2 PN-90/H-83159 N 650 250
LH17N37S2G PN-90/H-83159 N 480 15 155 – 220
310C45 BS3100 N
L140H20M2 PIOMA O 380
452 C 11 BS 3100 N 620 770 12
GX40CrNiSi274 DIN 17465 S lub N 200-300
EN 10295 S or N
GX40CrSi23 DIN 17465 S lub N 200-300
S or N
LH28N7G2S2 wg.specyfikacji

Rodzaje obróbki cieplnej (Kinds of heat treatment):

  • N – normalizacja (normalization)
  • U – ulepszanie (quenching and tempering)
  • O – odpuszczanie (tempering)
  • P – przesycanie (hyperquenching)
  • Z – zmiękczanie (soft annealing)
  • H – hartowanie (hardening)
  • NO – normalizacja z odpuszczaniem (normalization with tempering)
  • S – bez obróbki cieplnej (without heat treatment)

Contact

Pioma-Odlewnia Sp.z o.o.
ul. Romana Dmowskiego 38
97-300 Piotrków Trybunalski
Poland

KRS 0000287707,
Regon: 100398488,
VAT EU NO. PL7712766908

phone: +48 44 648 95 78
fax: +48 44 649 22 32
e-mail: pioma-odlewnia@pgosa.pll

Send enqiry

ico_gplus